Semiconductor device including ion implantion compensation region in cell array region

ABSTRACT

A first mask which is formed which exposes a cell array region and a peripheral circuit region of a semiconductor substrate. The cell array region and the peripheral circuit region are of a same conductive MOS type. Then, a preceding ion implantation process is implemented in both the cell array region and the peripheral circuit region utilizing the first mask. The preceding ion implantation process has ion implantation parameters corresponding to first implantation design specifications of one of the cell array region and the peripheral circuit region. Then, a second mask is formed which shields the one of the cell array region and the peripheral circuit region and which exposes the other of the cell array region and the peripheral circuit region. A subsequent ion implantation process is then implemented in the other of the cell array region and the peripheral circuit region utilizing the second mask. The subsequent ion implantation process has ion implantation parameters which compensate for a difference between the ion implantation parameters of the preceding implantation process and second implantation design specifications of the other of the cell array region and the peripheral circuit region.

CROSS-REFERENCE TO RELATED APPLICATIONS

This is a divisional of application Ser. No. 09/657,185, filed Sep. 7,2000, now U.S. Pat. No. 6,518,149, which is incorporated herein byreference in its entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semiconductor device and to a methodof manufacturing the same, and more particularly, the present inventionrelates to a semiconductor device having improved properties and to amethod of manufacturing the same in which a number of process steps isreduced by controlling ion implantation process parameters in aperipheral circuit region and a cell array region.

2. Description of the Related Art

Recently, as the use of computers in information media is expanding,rapid developments in semiconductor memory devices have also takenplace. That is, highly integrated devices having improved reliabilityand response times have been developed, resulting in semiconductormemories with high operational speeds and large storage capacities.

Highly integrated semiconductor devices are obtained by preciseelectrical isolation of various elements such as transistors, diodes,resistors, and the like formed on a semiconductor substrate. Isolationparameters are adopted at an early stage of the manufacturing processand define the size of an active region and process margins ofsubsequent processes.

Generally, the degree of integration of semiconductor devices hasexhibited a fourfold increase every three years, while the physical areaof the devices has only increased 1.4 times over that same period. Thus,the pitch size between elements has been reduced. As the pitch sizebetween elements continues to be reduced, it becomes difficult tomanufacture a device having satisfactory dielectric and refreshcharacteristics. The process of isolating an appropriately sized portionwithin a limited cell array region is one of the most difficult tasksassociated with achieving highly integrated semiconductor devices.

Currently, an isolation method utilizing poly spacer local oxidation iswidely used for the manufacture of active patterns having small pitchsizes. However, the resulting profile becomes distorted due to theformation of a bird's beak at the side portion of the field oxide. Thisresults in deterioration of the refresh characteristic.

To improve upon drawbacks associated with this problem, an ammonia (NH₃)plasma process is utilized to increase the effective channel length andto compensate for the thickness of the field oxides. In this method, thegrowth of the bird's beak by an oxidation of the side portion of thefield oxide can be restrained through nitrification of the surfaceportion of the field oxide by the ammonia plasma.

The nitrification reduces the oxidation of the side portion of the fieldoxides, thereby increasing their thicknesses. In particular, thethickness of the field oxides can be increased by about 200 Å using theammonia plasma treatment and this increases the effective field lengthto about 150 Å. As such, this method advantageously results in increasedprocess margins. However, the manufacturing process as a whole becomesmore complicated.

In another method of increasing isolation, a channel stopping ionimplantation is implemented under the active region. The ionimplantation is carried out by applying high energy to ions andinjecting the ions to penetrate the surface of a solid to be injected.Through the ion implantation, the number of impure elements and thejunction depth of the active region can be correctly controlled. Inaddition, since the processing temperature is low, a photoresist layercan be utilized as a protection layer and the concentration of theinjected impurity is almost uniform from the surface of a wafer.Further, the lateral spread of the impurity with respect to the verticalplane of the wafer surface is even less than that obtained by thermalspread.

For the silicon wafer, trivalent boron(B), pentavalent phosphor(P),arsenic(As) and the like can be utilized as the impurities. Since theseelements do not have gaseous phases at ambient temperature, gaseousmolecules including these impurities are utilized. BF₃, BCl₃, and thelike can be exemplified as the molecules including boron, PH₃ can beutilized as the molecules including phosphor, and AsH₃ can be utilizedas the molecules including arsenic. The ion implanting process will beschematically explained for implanting boron ions by utilizing BF₃ gas.

First, BF₃ gas molecules are introduced into a gas room so that themolecules and thermal electrons emitted from a heated filament collide.At this time, the thermions are accelerated by applying a voltagedifference of about 100V to increase an ionization degree of the BF₃ gasmolecules and a magnetic field is applied to increase the collisionprobability. From the collision of the emitted thermions and the BF₃molecules, dissociated ions such as ₁₀B⁺, F₂ ³⁰, ₁₁BF⁺, ₁₁B⁺, and thelike are produced and desired, ₁₁B⁺ ions are selected and accelerated byan appropriate magnetic field in a sorter. (The numbers preceding theletter B designate atomic weights of boron.)

After extracting the desired ions at the plasma state, a high energy isapplied to accelerate the ions so that the ions impact the surface ofthe wafer, and the thus accelerated ions are injected into the wafer. Atthis time, the applied energy determines the junction depth. In order tocontrol the concentration of the impurity, the amount of ions per unitarea (atoms/cm²), that is, dose is controlled. The ion implanted depthis controlled by the acceleration energy (eV) of the injected ions.

One important defect in the ion implanting process is a damage impartedon the crystal lattice of a single crystal silicon wafer after thecollision of the ions of high energy onto the wafer. To recover thedamage and to activate the injected impurities, an annealing at about900-1000° C. is implemented after the completion of the ion implantationprocess. Further, drawbacks in applying a high voltage and anintroduction of poisonous gases accompany the ion implantation process.Nevertheless, the ion implantation process is commonly utilized for theformation of a P-well and N-well, for the control of a thresholdvoltage, and for the formation of a source/drain region.

The ion implantation process is utilized to overcome the problems causedby different processing parameters for forming a cell array region and aperipheral circuit region. For example, U.S. Pat. No. 5,576,226 (issuedto Hwang) discloses a method for controlling the thickness of a gateoxide layer by selectively injecting oxidation promoting ions oroxidation retarding ions into a cell array region and a peripheralcircuit region. In addition, U.S. Pat. No. 5,780,310 (issued to Koyama)discloses a method for forming a cell array region on a recess having afirst impurity concentration and a peripheral circuit region having asecond impurity concentration so that the cell array region is formedfrom a lower portion than the peripheral circuit region.

Commonly, the channel stopping ion implantation is carried out afterforming the N-well/P-well and Si₃N₄/SiO₂ pattern. Through utilizing theSi₃N₄/SiO₂ pattern, B⁺ ions are injected for the P-well and P⁺ ions areinjected for the N-well. This channel stopping ion implantation also isreferred to as a field ion implantation.

Practically, the field ion implantation is separately implemented forthe cell array region and the peripheral circuit region by utilizingdifferent masks even for the same conductive type MOS regions such asNMOS or PMOS regions. The two regions have different ion implantingparameters because the thickness of a field oxide at the cell arrayregion is about 1500 Å and that of the peripheral circuit region isabout 2000 Å. Although the formation of the field oxides is carried outsimultaneously for the two regions, the thicknesses of the field oxidesat the two regions become different because the critical dimension atthe cell array region is narrower than that at the peripheral circuitregion.

Similarly, the field ion implantation processes at the NMOS cell arrayregion and the NMOS peripheral circuit region are carried out byutilizing different photo masks. Accordingly, when a photoresist patternis formed by utilizing a photo mask, all the ion implantation processesapplicable to an exposed region, such as an ion implantation for theformation of a well, a field ion implantation, and an ion implantationfor controlling a threshold voltage are continuously carried out. Then,another photoresist pattern is formed by utilizing another photo mask tocontinuously implement corresponding ion implantation processes for anexposed region.

Hereinafter, an ion implantation method for a device having an NMOS cellarray region and a CMOS peripheral circuit region will be explained indetail.

FIGS. 1A to 1C illustrate a conventional ion implantation method for adevice having an NMOS cell array region CN and a first and a secondperipheral circuit regions PN-1 and PN-2 of a CMOS type.

Referring to FIG. 1A, a photoresist pattern 11 for shielding NMOS typecell array region CN and PMOS type second peripheral circuit region PN-2and for exposing NMOS type first peripheral circuit region PN-1 isformed on a substrate 10. An ion implantation for the formation of aP-well, field ion implantation, and an ion implantation for controllinga threshold voltage for first peripheral circuit region PN-1 arecontinuously implemented.

Referring to FIG. 1B, a photoresist pattern 12 for shielding cell arrayregion CN and first peripheral circuit region PN-1 and for exposingsecond peripheral circuit region PN-2 is formed. An ion implantation forthe formation of an N-well, field ion implantation, and an ionimplantation for controlling a threshold voltage for second peripheralcircuit region PN-2 are continuously implemented.

Referring to FIG. 1C, a photoresist pattern 13 for shielding first andsecond peripheral circuit regions PN-1 and PN-2 and for exposing cellarray region CN is formed. An ion implantation for a formation of aP-well, field ion implantation, and an ion implantation for controllinga threshold voltage for cell array region CN are continuouslyimplemented.

As shown in the figures, the ion implantation processes for firstperipheral circuit region PN-1 and cell array region CN are separatelyimplemented even though they are the same NMOS type. The kind of ions,applied energy, and dose for each ion implantation process will beexemplified for first peripheral circuit region PN-1 and cell arrayregion CN. The explanation on second peripheral circuit region PN-2 ofthe PMOS type will be omitted.

For the first peripheral circuit region PN-1, the ion implantingparameters for formation of the P-well are ₁₁B⁺, 500 KeV, 1.0×10¹³; theion implanting parameters for formation of the field ion implantationare ₁₁B⁺, 120 KeV, 9.0×10¹²; and the ion implanting parameters forcontrol of the threshold voltage are ₁₁B⁺, 50 KeV, 1.0×10¹². Likewise,for the cell array region CN, the ion implanting parameters for theformation of the P-well is ₁₁B⁺, 500 KeV, 1.0×10¹³; the ion implantingparameters for formation of the field ion implantation are ₁₁B⁺, 100KeV, 7.5×10¹²; and the ion implanting parameters for control of thethreshold voltage are ₄₉BF₂ ⁺, 50 KeV, 6.2×10¹². (The numeral 11 of ₁₁B⁺indicates the atomic weight of boron and the numeral 49 of ₄₉BF₂ ⁺indicates the molecular weight of BF₂ ⁺.) The differences in the fieldion implanting parameters are attributed to the difference inthicknesses of the field oxides at the two regions. That is, since thefield oxide at the peripheral circuit region is thicker than that atthe, cell array region, the parameters applied for the peripheral regionis stronger.

In conclusion, even though the parameters for the formation of the wellsare the same for the two regions, the ion implantation processes areseparately implemented because the parameters for the subsequent ionimplantation processes are different. In the above-describedconventional method, a large number of process steps are required forthe manufacture of the semiconductor devices. Thus, the manufacturingprocess is complicated and the productivity (production rate) of thedevice is very low.

SUMMARY OF THE INVENTION

Accordingly, it is an object of the present invention to provide anadvantageous method for manufacturing a semiconductor device which hasreduced processing steps and an improved productivity.

It is a further object in the present invention to provide asemiconductor device having improved properties which can bemanufactured by such an advantageous method.

According to one aspect of the present invention, a semiconductor deviceis provided which includes a cell array region and a peripheral circuitregion. The cell array region and the peripheral circuit region havecorresponding ion implanted regions of a same object and a sameconductive MOS type. Further, the cell array region includes a first ionimplanted region which has a same depth and dose as an ion implantedregion formed on the peripheral circuit region, and a second ionimplanted compensation region. The ion implanted region can be formed byfield ion implantation process or ion implantation process forcontrolling a threshold voltage. The second ion implanted compensationregion can be formed above the first ion implanted region from a bottomportion of a substrate or a depth of the second ion implantedcompensation region can be the same as a depth of the first ionimplanted region.

According to another aspect of the present invention, a method ofmanufacturing a semiconductor device is provided which includes forminga first mask which exposes a cell array region and a peripheral circuitregion of a semiconductor substrate. The cell array region and theperipheral circuit region having a same conductive MOS type. Then, apreceding ion implantation process is implemented in both the cell arrayregion and the peripheral circuit region utilizing the first mask. Thepreceding ion implantation process has ion implantation parameterscorresponding to first implantation design specifications of one of thecell array region and the peripheral circuit region. Then, a second maskis formed which shields the one of the cell array region and theperipheral circuit region and which exposes the other of the cell arrayregion and the peripheral circuit region. Then, a subsequent ionimplantation process is implemented in the other of the cell arrayregion and the peripheral circuit region utilizing the second mask. Thesubsequent ion implantation process has ion implantation parameterswhich compensate for a difference between the ion implantationparameters of the preceding implantation process and second implantationdesign specifications of the other of the cell array region and theperipheral circuit region.

According to still another aspect of the present invention, a method ofmanufacturing a semiconductor device is provided with includes forming afirst mask which exposes a cell array region and a peripheral circuitregion of a semiconductor substrate, the cell array region and theperipheral circuit region each being of a same conductive MOS type.Then, a first ion implantation for forming a well, a second ion ionimplantation for forming a field, and a third ion implantation forcontrolling a threshold voltage are conducted in both the cell arrayregion and the peripheral circuit region utilizing the first mask. Ionimplantation parameters of the first, second and third ion implantationscorrespond to implantation design specifications of the peripheralcircuit region and include an implantation angle of about 7° fromnormal. Then, a second mask is formed which shields the peripheralcircuit region and which exposes the cell array region. Then, a fourthion implantation for forming a field and a fifth ion implantation forcontrolling a threshold voltage are conducted in the cell array regionutilizing the second mask. Ion implantation parameters of the fourth andfifth ion implantations compensate for a difference between the ionimplantation parameters of the second and third implantation processesand implantation design specifications of the cell array region andinclude an implantation angle of about 0° from normal.

BRIEF DESCRIPTION OF THE DRAWINGS

The above objects and advantages of the present invention will becomemore apparent by describing in detail preferred embodiments thereof withreference to the attached drawings in which:

FIGS. 1A to 1C illustrate a method for implanting ions onto a cell arrayregion and a peripheral circuit region according to the conventionalmethod;

FIGS. 2A to 2C illustrate a method for implanting ions onto a cell arrayregion and a peripheral circuit region according to an embodiment of thepresent invention;

FIG. 3 is a cross-sectional view of a semiconductor device forillustrating a relation between an applied energy and a depth of an ionimplanted region according to the present invention;

FIG. 4 is a cross-sectional view of a semiconductor device forillustrating a relation between an ion implanting angle and a depth ofan ion implanted region according to the present invention;

FIG. 5 is a graph for explaining a variation of an ion implanted regionaccording to an applied energy and an ion implanting angle at a fieldregion;

FIG. 6 is a graph for explaining a variation of an ion implanted regionaccording to an ion implanting angle at an active region; and

FIG. 7 is a cross-sectional view of a semiconductor device forillustrating ion implanted regions according to an embodiment of thepresent invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Hereinafter, embodiments of the present invention will be explained inmore detail with reference to the accompanying drawings. However, itshould be understood that the present invention is not limited to thefollowing embodiments.

FIGS. 2A to 2C illustrate a method of implanting ions onto an NMOS typecell array region CN, an NMOS type first peripheral circuit region PN-1,and a PMOS type second peripheral circuit region PN-2, according to anembodiment of the present invention.

Referring to FIG. 2A, a photoresist pattern 21 is formed on a substrate20 so as to expose cell array region CN and first peripheral circuitregion PN-1 and so as to shield second peripheral circuit region PN-2.Then, ion implantation processes are implemented having parameters whichare appropriate for first peripheral circuit region PN-1. In thisembodiment, an ion implantation for forming a P-well, a field ionimplantation and an ion implantation for controlling a threshold voltageare implemented.

Referring to FIG. 2B, a photoresist pattern 22 is formed so as to exposesecond peripheral circuit region PN-2 and so as to shield cell arrayregion CN and first peripheral circuit region PN-2. Then, an ionimplantation is implemented having parameters which are appropriate forthe second peripheral circuit region PN-2. In this embodiment, an ionimplantation for forming a P-well, a field ion implantation and an ionimplantation for controlling a threshold voltage are implemented.

Referring to FIG. 2C, a photoresist pattern 23 is formed so as to exposecell array region CN and so as to shield first and second peripheralcircuit regions PN-1 and PN-2. Then, subsequent ion implantationprocesses are implemented to effect compensation. That is, as notedabove in connection with FIG. 2A, ions have been implanted onto cellarray region CN using implantation parameters which are appropriate forthe first peripheral circuit region PN-1. Thus, in the cell array regionCN, it is necessary to compensate for the resultant difference fromdesired implantation characteristics obtained by the precedingimplantation processes. However, the ion implantation parameters for theformation of wells are the same for both the cell array region CN andfirst peripheral circuit region PN-1. Therefore, it is not necessary tocompensate for the well formation in the cell array region CN, andinstead compensation for the field ion implantation and the ionimplantation for controlling the threshold voltage is all this isneeded.

In comparing the present invention with the convention method of FIGS.1A to 1C, the number of the utilized masks is the same. However, asexplained above, the P-well formation process in the cell array regioncan be omitted in the present invention, thus reducing the number ofimplantation processing steps. In addition, the ion implantingparameters for the subsequent compensation processes are moderated.

FIG. 3 is a cross-sectional view of a semiconductor device whichillustrates a relationship between an applied energy and a depth of anion implanted region. In the example of FIG. 3, only cell array regionCN and the peripheral circuit region PN-1 of the same NMOS type areshown, since the ion implantation of the PMOS type region PN-2 is thesame as that of the conventional method. Also, an explanation in whichthe cell array region and one of peripheral circuit regions are bothPMOS type regions is omitted below, since the described method appliedto the same NMOS type regions can be also applied to the same PMOS typeregions.

In FIG. 3, a device is separated into an NMOS type peripheral regionPN-1 and an NMOS type cell array region CN. Peripheral circuit regionPN-1 and cell array region CN respectively include first and secondP-wells 31 and 32, and first and second field oxides 51 and 52. Thethickness of field oxide 51 formed at peripheral circuit region PN-1 isabout 2000 Å and that of field oxide 52 at cell array region CN is about1500 Å. First and second gate oxides 71 and 72 of about 100 Å, first andsecond gate electrodes 63 and 64 and first and second impurity dopedregions 61 and 62 are formed between each field oxide 51 and 52.

By implementing a field ion implantation process, B⁺ ions, for example,are implanted into a region around an ion implanted line 40 asillustrated in FIG. 3. This ion implantation increases the isolationefficiency between elements. Appropriate ion implantation parameters foreach process is as follows. First, ion implantation parameters for theformation of P-wells on the cell array region and the peripheral circuitregion are the same, i.e., ₁₁B⁺, 500 KeV, 1.0×10¹³. Therefore, if an ionimplantation for the formation of the P-well on the peripheral circuitregion PN-1 is carried out utilizing the mask illustrated in FIG. 2A, adesired P-well is also obtained in the cell array region CN.

On the other hand, the parameters of the field ion implantation for theperipheral circuit region are ₁₁B⁺, 120 KeV, 7.2×10¹² and those for thecell array region are ₁₁B⁺, 100 KeV, 7.5×10¹². In this invention, thefield ion implantation is implemented utilizing the mask illustrated inFIG. 2A with parameters appropriate for the peripheral circuit region.In the present embodiment, however, these parameters are ₁₁B⁺, 110 KeV,7.2×10¹². When compared with the normal implantation parameters of theperipheral circuit region, the energy value is lowered in thisembodiment from 120 KeV to 110 KeV. This will decrease the energydifference of the normal energy value of 100 KeV for the cell arrayregion. Repeated experiments by the inventor demonstrate that this lowervalue does not affect the isolation characteristic for the peripheralcircuit region. The field ion implantation for the cell array region iscompensated by utilizing the mask illustrated in FIG. 2C with theimplantation parameters of ₁₁B⁺, 90 KeV, 1.5×10¹².

The implantation parameters for controlling the threshold voltage are₁₁B⁺, 50 KeV, 1.0×10¹² for the peripheral circuit region and are ₄₉BF₂⁺, 50 KeV, 6.2×10¹² for the cell array region. First, an ionimplantation with the parameters of ₁₁B⁺, 50 KeV, 1.0×10¹² isimplemented for the two regions by utilizing the mask illustrated inFIG. 2A. Then, the compensating ion implantation for the cell arrayregion is implemented with the parameters of ₄₉BF₂ ⁺, 50 KeV, 6.0×10¹²by utilizing the mask illustrated in FIG. 2C. The energy values requiredfor the two regions are the same and the applied dose is reduced alittle for the compensation process.

In summary, an ion implantation process for the formation of a well onthe peripheral circuit region (and the cell array region), a field ionimplantation of the peripheral circuit region, an ion implantationprocess for the control of the threshold voltage for the peripheralcircuit region, a compensating field ion implantation for the cell arrayregion and a compensating ion implantation process for the control ofthe threshold voltage are sequentially implemented.

When compared with the conventional method, a separate ion implantationprocess for the formation of the P-well in the cell array region isomitted in the present invention. In addition, subsequently implementedcompensating processes of the field ion implantation and thresholdvoltage control are carried out with new implantation parameters. Thenew parameters for the compensation processes are determined asdescribed below.

First, the parameters of the field ion implantation for the peripheralcircuit region are ₁₁B⁺, 120 KeV, 9.0×10¹² when implementing theconventional method as illustrated in FIG. 1A. On the other hand, theseparameters are ₁₁B⁺, 110 KeV, 7.2×10¹² when implementing the method ofthe present invention as illustrated in FIG. 2A, to obtain correspondingion implanted line 40. That is, the energy value and the dose arereduced in the present invention. This values are obtained by optimizingthe field ion implantation parameters on the cell array region. Animaginary second ion implanted region 42 is limited around ion implantedline 40 and second ion implanted region 42 is compared with a first ionimplanted region 41 which is formed by applying a lower energy than thatapplied for the second ion implanted region 42 and with a third ionimplanted region 43 which is formed by applying a higher energy thanthat for region 42.

A distance d₁ from first region 41 to an impurity doped region, forexample, a source region 61, is determined by the value of the appliedenergy. An appropriate dose corresponding to that distance isdetermined. If the applied energy decreases and ions are implanted ontosecond region 42, a distance d₂ from second region 42 to source region61 is obtained. Since distance d₂ is shorter than distance d₁, a refreshcharacteristic of a device having second region 42 becomes inferior to adevice having first region 41.

In the meantime, when a dose amount increases, a dielectric effectincreases while the refresh characteristic decreases. Accordingly, whenthe distance from the ion implanted region to the source region becomesshorter, the dose amount should be decreased, and when the distancebecomes longer, the dose amount should be increased to obtain anappropriate dielectric and refresh effect.

In FIG. 1A, the ion implantation is carried out by applying an energy of120 KeV with a dose of 9.0×10¹². In FIG. 2A, since an energy of 110 KeVis smaller than that applied in FIG. 1A, the dose is decreased to7.2×10¹² to obtain a similar dielectric and refresh characteristic withthose obtained by implementing the ion implantation by applying anenergy of 120 KeV and dose of 9.0×10¹².

Next, the compensating parameters of the field ion implantation for thecell array region will be explained. Conventionally, the parameters ofthe field ion implantation for the cell array region are ₁₁B⁺, 100 KeV,7.5×10¹². When compared with the conventional parameters, the parametersof the present embodiment of ₁₁B⁺, 110 KeV, 7.2×10¹² which areappropriate for the peripheral circuit region and are implemented byutilizing the mask illustrated in FIG. 2A, the energy is increased whilethe dose is decreased. That is, an appropriate and conventional ionimplanted region is third ion implanted region 43 and a distance fromthird region 43 to source region 61 is d₃. Practically, however, ionimplanted region is second region 42 around ion implanted line 40.Accordingly, an actual ion implanted region is deeper than the desiredregion.

To obtain an appropriate dielectric and refresh characteristic, ions areimplanted onto a fourth ion implanted region 44 which is shallower thanthe desired third region 43, thereby achieving compensation. Theresulting dielectric and refresh effect obtained by implanting ions ontosecond and fourth regions 42 and 44 will give the same effect obtainedby implanting ions onto third region 43. Since a distance d₄ from fourthregion 44 to source region 61 is very short, the dose amount isdetermined so as to be smaller than that corresponding to third region43.

As a result of repeated experiments, the present inventor found that thepreferred energy value applied for the subsequent field ion implantationprocess is about 0.7-1 times (preferably about 0.85-1 times) the energyvalue required for the cell array or peripheral circuit regions wherethe subsequent field ion implantation process is implemented when theion implantation processes for the cell array and peripheral circuitregions are separately implemented.

Further, a sum of doses applied for the preceding and subsequent fieldion implantation processes is about 1-1.3 times of a dose required forthe cell array or peripheral circuit regions where the subsequent fieldion implantation process is implemented when the ion implantationprocesses for the cell array and peripheral circuit regions areseparately implemented. In the preferred embodiment of the presentinvention, the energy value of 90 KeV and the dose amount of 1.5×10¹²was applied.

For the ion implantation for controlling the threshold voltage, thecompensating parameters can be determined in a similar manner asdescribed for the field ion implantation. The conventionally appliedparameters for the peripheral circuit region are ₁₁B⁺, 50 KeV, 1.0×10¹²,and for the cell array region are ₄₉BF₂ ³⁰ , 50 KeV, 6.2 ×10¹². In thisembodiment of the present invention, a preceding ion implantation iscarried out for both the peripheral circuit region and the cell arrayregion with the conventional parameters for the peripheral circuitregion shown above by utilizing the mask as in FIG. 2A. After that, asubsequent ion implantation is carried out for the cell array regionwith the compensating parameters of ₄₉BF₂ ⁺, 50 KeV, 6.0×10¹² byutilizing the mask as in FIG. 2C. Since the energy values for the tworegions are the same, the compensating parameters are determined byslightly changing the dose amount.

A sum of doses, applied for the preceding and subsequent ionimplantation processes for controlling the threshold voltages, ispreferably about 0.95-1.05 times of a dose required for the cell arrayor peripheral circuit regions where the subsequent ion implantationprocess for controlling the threshold voltage is implemented when theion implantation processes for the cell array and peripheral circuitregions are separately implemented.

The compensating parameters were obtained by optimization. However, thepresent invention is not limited to the optimized compensatingparameters.

When implementing the ion implantation process according to the methoddescribed above, the manufacturing process can be simplified, and thethus obtained device will exhibit the same or superior characteristicsrelative to devices obtained by the conventional method.

FIG. 4 is a cross-sectional view of a semiconductor device forillustrating a relation between an ion implanting angle and a depth ofan ion implanted region realized by the method of the present invention.

In a device having a small pitch size, a high concentration ionimplantation of a portion under a field oxide is required for preventinga deterioration of isolating properties. The above-described field ionimplantation is implemented for the isolation in the present invention.The concentration and Rp (projected range) of the ion implantation for asilicon substrate having a lattice structure change according to the ionimplantation angle. However, for an oxide, Rp does not change accordingto the ion implantation angle. Accordingly, the difference of Rp causedby the implantation angle changes a junction characteristic at thejunction of an active region and a field region.

ET (electric test) data for the active region and the field region whenthe ion implantation angles are 7° and 0°, are illustrated in Table 1.The parameters of the ion implantation were ₁₁B⁺, 100 KeV, 7.5×10¹².

TABLE 1 Implantation angle Vth J_BV C_Iso_BV 7° 1.17 8.35 4.2 0° 1.158.55 3.7

In Table 1, Vth represents a threshold voltage, J_BV represents ajunction breakdown voltage, and C_Iso_BV represents a field oxidebreakdown voltage. J_BV and C_Iso_BV show different aspects.

In a MOS device, an electron layer generated by a gate voltage forms aconductive channel between n+drain and source region. The gate voltageneeded for the generation of the conductive channel is referred to asthreshold voltage or pinch off voltage.

When excessive reverse voltage is applied to a PN junction diode and thevoltage exceeds a predetermined limit voltage, reverse current rapidlyincreases. This phenomenon is called junction breakdown and the limitvoltage is referred to as junction breakdown voltage. If an excessiveamount of voltage exceeding the breakdown voltage is applied to asemiconductor device, a damage is imported to the device.

By Table 1, it can be seen that the characteristics are improved at thejunction deteriorated at the field region when the ion implantationangle is changed from 7° to 0°.

A good isolation and refresh characteristic can be accomplished bycontrolling the ion implantation angle in view of a profile changeaccording to the crystal structures of silicon and oxide. That is, ifthe ion implantation angle is set near 0°, a doping concentration aroundjunction region can be reduced while maintaining constant a dopingconcentration under the field oxide.

FIG. 5 is a graph for explaining variations of an ion implanted regionwith respect to an applied energy and an ion implanting angle at a fieldregion, and FIG. 6 is a graph for explaining variations of an ionimplanted region with respect to an ion implanting angle at an activeregion. FIGS. 5 and 6 will be explained with reference to FIG. 4.

Referring to FIG. 5, a field oxide has a thickness of about 1500 Å. Lineh represents a doping profile obtained by applying an energy of 120 KeV,a dose of 1.0×10¹³ and an ion implantation angle of 7°, line irepresents a doping profile obtained by applying an energy of 100 KeV, adose of 1.0×10¹³ and an ion implantation angle of 0°, line j representsa doping profile obtained by applying an energy of 100 KeV, a dose of1.0×10¹³ and an ion implantation angle of 7°, and line k represents adoping profile obtained by applying an energy of 80 KeV, a dose of1.0×10¹³ and an ion implantation angle of 7°.

As the energy gradually decreases from 120 KeV to 100 KeV and 80 KeV,the depth of the ion implanted region from the surface of a substrategradually decreases to obtain ion implanted lines corresponding to afirst, a second and a third ion is implanted lines a, b and cillustrated in FIG. 4. On the contrary, when the applied energy valuesare the same and only the ion implanting angles are different, almostsimilar ion implanted lines are obtained as illustrated by graphs i andj and by a fifth ion implanted region 81 in FIG. 4.

Referring to FIG. 6, doping profiles can be seen for an active regionwhich has an oxide layer having a thickness of about 103 Å. The appliedenergy and dose were 100 KeV and 1.0×10¹³ and the ion implanted angleswere 0° for line 1, 1° for line m, and 7° for line n. Referring to FIG.4, as the ion implanting angle increases from 0° to 1° and 7°, the ionimplanted lines become deeper from a fourth implanted line d to a fifthand sixth ion implanted lines e and f at the active region. Distancesfrom each ion implanted region at the active region to source region 61is d₅, d₆ and d₇.

In conclusion, when other ion implantation parameters are same, betterrefresh 5characteristic can be obtained by setting the ion implantingangle near 0°. However, when an ion beam is injected into the samedirection of a crystal axis, an energy loss becomes small and the Rpincreases. That is, the Rp is dependent on an angle between the ion beamand the crystal axis and an amount of ion dose. To prevent a channelingeffect, a wafer is inclined to about 7° with respect to an incident ionbeam. Practically, ions are injected with some deviations and thedisplacement owing to the angle deviation appears less with the angle of7° than with the angle of 0°. In practice, the angle of 7° is appliedwhen the dose amount is large and the angle of 0° is applied when thedose amount is small.

For the present invention, the angle of 7° is applied in the precedingfield ion implantation in which the dose amount is large, while theangle of 0° is applied in the subsequent compensating field ionimplantation in which the dose amount is small.

FIG. 7 is a cross-sectional view of a semiconductor device forillustrating ion implanted regions according to a preferred embodimentof the present invention.

At NMOS type peripheral circuit region PN-1, a first ion implantedregion for forming a well 33, a first field ion implanted region 35, anda first ion implanted region for controlling a threshold voltage 38 areformed from a bottom portion of a substrate 30. At NMOS type cell arrayregion CN, a second ion implanted region for forming a well 34, a secondfield ion implanted region 36, a compensating field ion implanted region37, and a second ion implanted region for controlling a thresholdvoltage 39 are formed. Since the compensating field ion implantationregion 37 in the cell array region is formed at the same region of thesecond ion implanted region for controlling the threshold voltage 39,region 37 is not separately formed. Therefore, the depth of region 39 isthe same with that of first ion implantation region for controllingthreshold voltage 38. However, ₁₁B⁺ ions and ₄₉BF₂ ⁺ ions are present atregion 39 while only ₁₁B⁺ ions are present at region 38.

The preferred embodiment for manufacturing a device illustrated in FIG.7 will be explained in more detail below. In this embodiment, a DRAMdevice having an NMOS type cell array region and a CMOS type peripheralcircuit region is illustrated.

First, on a cell array region and a peripheral circuit region for theformation of an NMOS, an n-type silicon substrate was oxidized for abuffer oxidation to a thickness of about 450 Å and silicon nitride wasdeposited to a thickness of 1600 Å to form an oxide layer and a siliconnitride layer. The silicon nitride layer was etched by utilizing aphotoresist pattern and then, photoresist was removed. A field oxidationwas implemented by utilizing a nitride pattern at about 900° C. Thethickness of the thus obtained field oxide was about 1500 Å at the cellarray region and about 2000 Å at the peripheral circuit region.

A photoresist pattern was formed for exposing the NMOS-type peripheralcircuit region and the NMOS-type cell array region as illustrated inFIG. 2A. A boron ion implantation was implemented with parameters of₁₁B⁺, 500 KeV, 1.0×10¹³ to form P-wells at the cell array region and aportion of the peripheral circuit region. After completing the ionimplantation, a heat treatment was carried out at about 1000° C. forabout 630 minutes under a nitrogen gas flow, and then for 30 minutesunder an oxygen gas flow at the same temperature. Then, a field ionimplantation process was implemented with parameters of ₁₁B⁺, 110 KeV,7.2×10¹² and an ion implantation for controlling the threshold voltagewas carried out with parameters of ₁₁B⁺, 50 KeV, 1.0×10¹².

Thereafter, a photoresist pattern was formed for exposing a PMOS-typeperipheral circuit region as illustrated in FIG. 2B. An ion implantationfor the formation of a well, a field ion implantation, and an ionimplantation for controlling a threshold voltage were continuouslycarried out.

A photoresist pattern for exposing the cell array region was formed asillustrated in FIG. 2C and a compensating field ion implantation wascarried out with parameters of ₁₁B⁺, 90 KeV, 1.5×10¹². A compensatingion implantation for controlling the threshold voltage was carried outwith parameters of ₄₉BF₂ ⁺, 50 KeV, 6.2×10¹² by utilizing the samephoto-resist mask.

Then, a semiconductor device was manufactured by a conventional method.That is, a first oxide layer is formed on an active region of thesemiconductor substrate, in which the active region and a field regionare separated by the field oxide, by utilizing a thermal oxidationmethod. Then, a gate electrode is formed as follows. A first conductivelayer was formed on the first oxidation layer by depositing a conductivematerial such as polysilicon doped with impurities, and a secondconductive layer is formed by utilizing material such astungsten-silicide (WSi_(x)). On the second conductive layer, a firstdielectric layer of silicon nitride (SiN) is formed. The firstdielectric layer functions to protect the second conductive layer duringan implementation of subsequent etching and ion implantation processes.Then, a second oxidation layer is formed by using high temperature oxide(HTO). The second oxidation layer is utilized as an etching stopperduring an etching process for forming a spacer.

A photoresist pattern is then formed on the second oxidation layer and agate electrode is obtained by continuously and anisotropically etchingthe second oxidation layer, the first dielectric layer, the secondconductive layer, the first conductive layer and the first oxidationlayer.

An n-type impurity is doped onto the exposed active region of thesemiconductor substrate to form a source/drain diffusion region of atransistor. During the ion doping, the gate electrode acted as a mask.

On the substrate in which the gate electrode is formed, dielectricmaterial such as BPSG (borophosphosilicate glass) is deposited to form adielectric interlayer. Then, a photoresist pattern was formed on thedielectric interlayer and an exposed portion is etched to form a contacthole. Metal is then deposited to form a contact and wiring layer tomanufacture a semiconductor device according to the method of thepresent invention.

The above-described method of the present invention can be applied forthe formation of ion implanted regions for a PMOS-type cell array regionand a PMOS-type peripheral circuit region.

In addition, a LOCOS (local oxidation of silicon) method was applied forthe isolation of the elements in the preferred embodiment of the presentinvention. However, the present invention can be applied to a deviceutilizing an STI (shallow trench isolation) method. Particularly,because the depth of the trench at the peripheral circuit region and atthe cell array region are almost the same, the parameters of field ionimplantations for the two regions are almost the same. When the fieldion implantation parameters are similar but somewhat different for thetwo regions, the above-described method of the present invention can beapplied and when the field ion implantation parameters are same, thecompensating field ion implantation for the cell array region can beomitted.

According to the method of the present invention, separately implementedion implantation processes for the peripheral circuit region and thecell array region can be carried out in a closely connected manner, andtherefore, the number of steps of the ion implantation process can bereduced to simplify the manufacturing of the semiconductor, therebyimproving the productivity of the devices. In addition, since moderateion implantation parameters accompany the subsequent compensatingprocess, an ion implantation angle of 0° can be applied for thecompensating ion implantation. Thus, a semiconductor device havingimproved properties can be realized.

While the present invention is described in detail referring to theattached embodiment, various modifications, alternate constructions andequivalents may be employed without departing from the true spirit andscope of the present invention.

What is claimed is:
 1. A semiconductor device comprising a cell arrayregion and a peripheral circuit region which have corresponding ionimplanted regions of a same object and a same conductive MOS type,wherein said cell array region comprises: a first ion implanted regionwhich has a same depth and dose as a corresponding ion implanted regionformed on said peripheral circuit region; and a second ion implantedcompensation region, wherein said peripheral circuit region is devoid ofa corresponding ion implanted region at a same depth as the second ionimplanted compensation region in said cell array region.
 2. Thesemiconductor device as claimed in claim 1, wherein said correspondingion implanted region is a field ion implantation or a threshold voltagecontrol ion implantation.
 3. The semiconductor device as claimed inclaim 1, wherein said second ion implanted compensation region islocated above said first ion implanted region from a bottom portion of asubstrate.
 4. The semiconductor device as claimed in claim 1, whereinsaid conductive MOS type is an NMOS type or a PMOS type.
 5. Asemiconductor device comprising a cell array region and a peripheralcircuit region which have corresponding ion implanted regions of a sameobject and a same conductive MOS type, wherein said cell array regioncomprises: a first ion implanted region which has a same depth and doseas a first corresponding ion implanted region formed on said peripheralcircuit region; and a second ion implanted compensation region which hasa same depth and a different dose as a second corresponding ionimplanted region formed in said peripheral circuit region.
 6. Thesemiconductor device as claimed in claim 5, wherein said second ionimplanted region comprises ₁₁B⁺ ions and ₄₉BF₂+ ions and said secondcorresponding ion implanted compensation region comprises ₁₁B⁺ ions.